Kinkou-96 Coper Aleoy (Cu-9ni-6sn C72700)
1. Halabuurka kiimikada ee C72700
| Nooc | Ni | Sn | Mn | Pb | Zn | Fe | P | Cilado | Cu |
| C72700 | 8.5-9.5 | 5.5-6.5 | 0.05-0.3 | ≤0.03 | ≤0.15 | ≤0.05 | ≤0.05 | ≤0.5 | Itashirid |
2. Guryaha jirka ee C72700
| Cucid | 8.9 | (G / cm3) |
| Dhibcaha dhalaalaya | 968-1078 | (℃) |
| Feejignaanta kuleylka kuleylka | 17.25 | (X10-6/ ℃) 20-200 ℃ |
| Modulus laastikada | 120 | (GPA) |
| Dib-u-hakinta korantada ee 20 ℃ |
| μω * cm |
| Deray | ≤19.5 |
|
| Xadhig roonaan | ≤5 |
|
| Wadahadalka korantada (Iacs,%) |
| (% Iacs) |
| ≥9 |
| |
| Xaddidaynta roobka (3 saacadood) | ≥12 |
|
| Modulus torsonal | 50 | (GPA) |
| Xadgudubka kuleylka ah ee 20 ℃ | 53.6 | (W / mk) |
| Datanaanta xoogga daalka | 450 | (MPA) |
3. Guryaha farsamada / gobolka ee C72700
1) Alaabada la duubay
| Sheegid | Adkayn | Awooda TSensile | Xoog wax soo saar | Elonkaaion | Dhaaf * | Adkaanta, dabaqadka iyo astaamaha daalka daalka (MPA) | ||
| HV | RM (MPA) | RP 0.2 (MPA) | A50mm (%) | Longintidinal // | Targesverse | Longintidinal // | Targesverse | |
| Darida | ||||||||
| TB | 90-125 | 420-500 | ≥200 | ≥30 | 0.2 | 0.2 | 302 | 220 |
| Daboolka / qabowga | ||||||||
| Td1 | 140-180 | 460-560 | ≥300 | ≥15 | 0.2 | 0.2 | 216 | 359 |
| Td2 | 160-200 | 540-640 | ≥400 | ≥10 | 0.2 | 0.2 | 275 | 390 |
| Td3 | 200-240 | 620-720 | 550 | ≥3 | 0.5 | 0.5 | 444 | 523 |
| Td4 | 220-260 | 700-820 | ≥600 | ≈1 | 2 | 1 | 467 | 568 |
| TDX | ≤320 | ≥780 | 650 | ≈1 | 10 | 2 | 472 | 613 |
| Daweynta kuleylka / roobka | ||||||||
| TF | 230-270 | 740-860 | ≥510 | ≥10 | 0.5 | 0.5 | 566 | 634 |
| Daweynta kuleylka / qabowga qaboojinta | ||||||||
| Th1 | 270-310 | 850-950 | 650 | ≥8 | 0.5 | 0.5 | 684 | 724 |
| Th2 | 290-320 | 880-980 | ≥720 | ≥8 | 1 | 1 | 730 | 770 |
| Th3 | 310-340 | 950-1050 | ≥800 | ≥4 | 1 | 1 | 829 | ≥840 |
| Th4 | 320-360 | 1000-1100 | ≥900 | ≈3 | 2 | 2 | 8330 | ≥840 |
| Thx | ≤390 | ≥1050 | 950 | ≈1 | / | / | 8330 | ≥840 |
| *: Sida laga soo xigtay Din 5011 (25/10/85), oo foorarsata 90 ° jihada duufaanka, u qaybi meesha ugu yar ee foorarsan dhumucda si loo go'aamiyo riyaha R / T | ||||||||
2) Alaabada la soo qaaday
| Sheegid | Adkayn | Awooda TSensile | Xoog wax soo saar | Elonkaaion | Isku-duwaha Ballaarinta |
| HV | RM (MPA) | RP 0.2 (MPA) | A50mm (%) | Z% | |
| Darida | |||||
| TB | ≤50 | 400-500 | ≥200 | ≥30 | ≥80 |
| Daboolka / qabowga | |||||
| Td1 | 150-180 | 500-580 | ≥300 | ≥10 | ≥75 |
| Td2 | 180-230 | 550-720 | ≥500 | ≥3 | ≥70 |
| Td3 | 220-260 | 700-800 | ≥600 | ≥2 | ≥65 |
| Td4 | 230-300 | 780-880 | ≥700 | ≥1.5 | ≥60 |
| TDX | 250-320 | 880-1000 | ≥800 | ≥0.1 | ≥50 |
|
|
|
|
|
|
|
| Sheegid | HV | RM (MPA) | RP 0.2 (MPA) | A50mm (%) | Z% |
| Daweynta kuleylka / roobka | |||||
| TF | ≤260 | 770-870 | ≥500 | ≥20 | ≥40 |
| Daweynta kuleylka / qabowga qaboojinta | |||||
| Th1 | 260-300 | 870-970 | ≥700 | ≥13 | ≥30 |
| Th2 | 290-310 | 930-1030 | ≥800 | ≥8 | ≥30 |
| Th3 | 310-330 | 1000-1100 | ≥900 | ≥5 | ≥30 |
| Th4 | 330-360 | 1100-1200 | ≥1000 | ≥2 | ≥30 |
| Thx | ≥350 | 1175-1300 | ≥1100 | ≥0.5 | ≥30 |
4. Dulqaadashada caadiga ah ee usha iyo siligga C72700
| Teeb ku qorid | Dhexroor | Dulqaadashada dhexroor | Dulqaadkii toosan | |||
| aasaasi ah | mm | aasaasi ah | mm | aasaasi ah | mm | |
| Silig | 0.2-0.39 | 6.35-9.9 | +/-.002 | +/- 0.05 | Dhererka = 10ft, weecashada <0.25 inji | Dhererka = 3048mm, zartins <.35mm |
| 0.4-0.74 | 10-18.9 | + 0.005 / -0 | + 0.13 / -0 | |||
| Ulley | 0.75-1.6 | 19-40.9 | + 0.02 / + 0.08 | + 0.5 / + 2.0 | Dhererka = 10ft, weecashada <0.5 inji | Dhererka = 3048mm, leexasho <12mm |
| 1.61-2.75 | 41-70 | + 0.02 / + 0.10 | + 0.02 / + 0.10 | |||
| 2.76-3.25 | 70.1-82 | + 0.02 / + 0.145 | + 0.02 / + 0.145 | |||
| 3.26-6.00 | 83-152.4 | + 0.02 / + 0.187 | + 0.02 / + 0.187 | |||
| <0.4 | 10 | +/-.002 | +/- 0.05 |
|
| |
5. Codsiga C72700
Ku beddelashada beryllium cootper coper ah
Waxaa loo isticmaalaa muraayadaha indhaha, koronto, koronto, elektronechechanical, elektiroonig, isku xirayaal, gawaarida, qalabka guryaha, warshadaha muuqaalka ah, qaybo u roga